Liquid bitumen waterproofing coating for cold application
TERALIT L is a liquid bitumen waterproofing coating based on distilled bitumen dissolved in organic solvent. It is designed for preparing concrete and metal surfaces using a cold application method, prior to laying bituminous waterproofing strips. The surface must be dry and well-cleaned. When used indoors, smoking, open flames, or sparking tools near the application area are prohibited. It is applied with a brush or roller in its cold state. Consumption is 0.3-0.5 kg/m2. Packaging is available in plastic containers of 5 and 10 liters.
Characteristic
|
EN standard
|
Unit of measure
|
Declared value
|
---|---|---|---|
Bitumen content
|
DIN 53215
|
% (m/m)
|
65 (±5%)
|
Softening point according to PK*
|
HRN EN 1427
|
°C
|
≥40
|
Flash point (COC)*
|
HRN ISO 2592
|
°C
|
≥35
|
Drying time (room temperature)
|
/
|
h
|
3-6
|
Density at 20°C
|
/
|
g/m³
|
0,930 (±10%)
|
Viscosity according to Ford ø 4mm
|
/
|
sec
|
90 (±20%)
|
Liquid bituminous waterproofing coating for cold application.
TERALIT L is a liquid bituminous waterproofing coating based on distilled bitumen dissolved in organic solvent. It is designed for preparing concrete and metal substrates using the cold application method, before laying bituminous waterproofing strips. The substrate must be dry and thoroughly cleaned. When used indoors, smoking, open flames, or sparking tools near the application area are not allowed. It is applied with a brush or roller in its cold state. Consumption rate is 0.3-0.5 kg/m2. It is packaged in plastic containers of 5 and 10 liters.
Characteristic
|
EN standard
|
Unit of measure
|
Declared value
|
---|---|---|---|
Bitumen content
|
DIN 53215
|
% (m/m)
|
65 (±5%)
|
Softening point according to PK*
|
HRN EN 1427
|
°C
|
≥40
|
Flash point (COC)*
|
HRN ISO 2592
|
°C
|
≥35
|
Drying time (room temperature)
|
/
|
h
|
3-6
|
Density at 20°C
|
/
|
g/m³
|
0,930 (±10%)
|
Viscosity according to Ford ø 4mm
|
/
|
sec
|
90 (±20%)
|
Bituminous waterproofing coating for hot application
TERALIT S/100 is a bituminous waterproofing coating based on oxidized bitumen, without added polymer modifiers, additives, or fillers. It is designed for preparing concrete and metal substrates using the hot application method, before laying bituminous waterproofing strips. The substrate must be dry and thoroughly cleaned.
TERALIT S/100 can also be used as a standalone waterproofing coating to protect concrete, metal, wood, and similar surfaces in conditions where it meets the waterproofing requirements of the surface in an environment subject to climatic conditions, with ambient temperatures ranging from 0°C to 70°C. It is applied in a molten state at approximately 170°C. Consumption rate is 1.5 – 2.0 kg/m². It is packaged in metal containers weighing approximately 23 kg.
Characteristic
|
EN standard
|
Unit of measure
|
Declared value
|
---|---|---|---|
Bitumen content
|
/
|
% (m/m)
|
100
|
Softening point according to PK*
|
EN 1427
|
°C
|
≥80
|
Flash point (COC)*
|
EN 1109
|
°C
|
≤0
|
Drying time (room temperature)
|
EN 1110
|
°C
|
≥80
|
Density at 20°C
|
/
|
%
|
0
|
Terrasit is the company that manufactures products from expanded polystyrene (EPS) and expanded polypropylene (EPP) for construction, industry, and packaging.
Branilaca grada b.b. – Industrijska zona, 75320
+387 35 705 163 info@terrasit.com
Terrasit d.o.o. 2023 © All rights reserved